三星18650锂电池

Nominal Capacity

2600mAh (0.2C, 2.75V discharge)

Minimum Capacity

2550mAh(0.2C, 2.75V discharge)

Charging Voltage

4.2 ±0.05 V

Nominal Voltage

3.7V

Charging Method

CC-CV

Charging Current

Standard charge: 1300mA

Rapid charge : 2600mA

Charging Time

Standard charge : 3hours

Rapid charge : 2.5hours

Max. Charge Current

2600mA(ambient temperature25℃)

Max. Discharge Current

5200mA(ambient temperature 25℃)

Discharge Cut-off Voltage

2.75V

Cell Weight

47.0gmax

Cell Dimension

Height : 65.00mm max

Diameter : 18.25mm max

Operating Temperature

Charge : 0 to 45℃

Discharge: -20 to 60℃

NO.

Items

Specifications

1

Mode

型号

18650

2

Size

尺寸

18*65（mm）

3

Charge voltage

充电电压

4.2V

4

Nominal voltage

标称电压

3.7V

5

Nominal capacity

标称容量

2600mAh

6

Charge current

充电电流

Standard Charging:：0.5C标准充电：0.5C

     Rapid charge：1.0C快速充电：1.0C

7

Standard Charging method

标准充电方法

0.5CCC（constant current）charge to 4.2V,then CV(constant voltage 4.2V)charge till charge current decline to≤0.05C

0.5CCC（恒流）充电至4.2V，再CV（恒压4.2V）充电直至充电电流≤0.05C

8

Charging time

充电时间

Standard Charging：3.0hours(Ref.)

            标准充电：5.0小时（参考值）

   Rapid charge：2hours(Ref.)

          快速充电：1小时（参考值）

9

Max.charge current

最大充电电流

1C（2600mAh）

10

Max.discharge current

最大放电电流

1C(2600mAh)

11

Discharge cut-off voltage

放电截止电压

2.75V

12

Operating temperature

工作温度

Charging：0℃~45℃

  充电：0℃~45℃

Discharging：0℃~45℃

放电：0℃~45℃

13

Storage temperature

储存温度

-20℃~ +60℃

14

Cell Weight

电芯重量

Approx：45g

约：45g  

序号

项目

测试方法

标准

1

过充实验

电池以0.2C₅A电流恒流放电至3.0V，以电流3 C₅限制电压5.0V的制式充电，5v恒压电流接近0，持续30分钟。

不爆炸、不起火

2

过放实验

电池完全充电后，在环境温度20±5℃的条件下,以0.2C₅A放电至终止电压后,外接30Ω负载电阻放电24h.

不爆炸、不起火

3

热冲击实验

将充满电的电池放在重力对流或循环空气的烘箱中进行加热，烘箱的温度以5±2℃的速率上升到130±2℃后保温10分钟。

不爆炸、不起火

序号

项目

测试方法

标准

1

高温实验

将充满电的电池在70℃环境中放置2小时。

电性能、外观不受影响

2

低温实验

将充满电的电池在-10℃的环境中放置2小时后在室温中放置3小时。

电性能、外观不受影响

3

高温高湿实验

将充满电的电池放入40±2℃、相对湿度为90％～95％的恒温湿箱中搁置48h后，取出电池在环境温度20±5℃的条件下搁置2h。

电性能、外观不受影响，包括包装。